• Superior chemical and abrasion resistance
• Medium viscosity
• Excellent bonding
• Highly resistant to cratering or blush
• Dries to a high gloss
• Low odor
• 100% solids, no solvents
• Cures in the presence of moisture and humidity with excellent mechanical properties

• Recommended for floor coating and bermed secondary containment areas where high concentrations of chemicals are used
• Application where increased resistance to acids, bases and solvents is desired
• Non-slip surfaces can be achieved with broadcast of quartz, aluminum oxide or other non-skid material

 

Solids by Volume	100%
VOCs (grams/liter)	0
Mixing ratio	2:1 by volume
Viscosity	500-800 cps, mixed
Pot Life (neat coating)	25-30 minutes
Application Temperature	55°F minimum, 100°F maximum
Maximum Re-coat Time	24 hrs.
Dry To Touch	6-8 hrs.
Light Traffic	14-16 hrs
Return To Service	24-36-hrs.
Full Cure	7 Days

 

 

Hardness (Shore D)	86+5
Tensile Strength (psi)	7000-8000	ASTM D-638
Tensile Elongation (%)	3.2	ASTM D-638
Flexural Strength	13000 – 13800	ASTM D-790
Compressive Strength (psi)	12000 – 14000	ASTM D-695
HDT (F)	140	ASTM D-648-264
Water Absorption (% gain) 24 hrs	<1
Bond Strength (psi) to concrete	>400, w/100% concrete failure

 

A thorough and complete mixing is critical. First mix each component separately. Proportion each component at the ratio of 2 parts A (resin) to 1 part B (hardener) by volume or if using 1-gallon kits, pour all of Part B (hardener) into Part A (resin). Mix for 3 – 5 minutes, scraping the mixing container sides and bottom regularly. Mix no more material than may be applied in 20 minutes.

 

Reagent	% Weight gain (loss)
Xylene	0.0
1,1,1 Trichloroethane	0.0
EB (Ethylene Glycol Monobutyl Ether)	2.4
Water (deionized)	1.2
10% Sodium Hydroxide	0.0
10% Sulfide Acid	0.0
10% Hydrochloric Acid	0.1
10% Acetic Acid	5.4
Synthetic Gasohol	0.0
JP-4, JP-5, JP-7, JP-8	0.0

 

Reagent	% Weight gain (loss)
Toluene	2.3
MEK	2.3
Ethyl Alcohol	6.9
5% Detergent Solution	0.0
50% Sodium Hydroxide	(0.2)
70% Sulfuric Acid	0.2
5% Acetic Acid	2.6
Skydrol	(0.03)
Mogas, Diesel	0.0
Diethylene Glycol Monomethyl Ether	0.0